Quick Details

  • Place of Origin: Hebei, China (Mainland)
  • Brand Name: SINIPEC
  • Model Number: PP R

Packaging & Delivery

Packaging Details: 25kg bag .PE inside ,PP outside .
Delivery Detail: within 2 weeks

Specifications

pp film grade/ pp rawmaterial
process type: virgin and recycled
color: white,black, red, green, blue, yellow, etc

Specifications

 

PP plastic raw material/virgin PP granules/PP injection grade
polypropylene, PP raw material, virgin&recycled PP granules
PP

 

                   PP plastic raw material/virgin PP granules/PP injection grade

 

PP/HDPE/LDPE/LLDPE/PVC/HIPS/GPPS/PS 

1/ Properties:

 

1.crystal or milky white
2.non-toxic, odorless, low density
3.strength, stiffness, hardness and heat resistance are superior to low pressure polyethylene.

 

  Light and billig health resistance to high temperature resistance wet, recycling easy process molding, transparency and surface gloss, and mechanical properties of the higher good non-toxic relative density low resistance to chemicals such good properties, and high ratio of performance.

 

2/ Specification:

 

Properties

Unit

Test method

Value

Melt Flow Rate

 

 

 

Melt flow rate(230°C/2.16KG)

g/10min

ISO 1133

12

Mechnical Properties

 

 

 

Tensile modulus of elasticity(v=1mm/min)

Mpa

ISO 527-2

1550

Tensile yield at stress(v=50mm/min)

Mpa

ISO 527-2

35

Tensile yield at strain (v=50mm/min)

%

ISO 527-2

8

Tensile strain at break (v=50mm/min)

%

ISO 527-2

>50

Charpy impact strength unnotched(+23°C)

kJ/m2

ISO 179/1eU

110

Charpy impact strength notched(+23°C)

kJ/m2

ISO 179/1eA

3.0

Izod Impact strength notenched(+23°C)

kJ/m2

ISO 180/1A

3

Ball indentation hardness(H 358/30)

Mpa

ISO 2039-1

78

Thermal Properties

 

 

 

Melting point,DSC

°C

ISO 3146

163

Heat deflection temperature (0.45Mpa)                    

°C

ISO 75-2

85

Vicat softening temperature  VST/A50(10N)

°C

ISO 306

154

Other Properties

 

 

 

Density

g/cm3

ISO 1183

0.91

 

 PP Copolymer

 

Tests
Value
Unit
Melt Flow Rate
45
g/10min
Density
0.90
G/cm3
Elongation Stress 
10
%
Flexural modulus
14
Mpa
Rockwell hardness
95
R scale
IZOD impact strength
6.5
kg.cm/cm
Vicat softening point
152
°C
Heat distortion temperature
125
°C

 


PP Random Copolymer (PPR)

 

Tests
Value
Unit
Method
Melt Flow Rate (MFR)
0.45
g/10min
GB 3682
Density
0.91
g/cm3
ASTM D-1505
Tensile Strength at Yield
24
Mpa
GB 1040
Elongation at Break
750
%
GB 1040
Rockwellhardness
85
J/M
GB 9342
 Izod impact strength
65
J/M
ASTM D-256

 

 

 3/ Application:

 

Injectionvalve, fittings, crates, automotive, closure, appliances, kettles, food containers, housewares, toys, non-prefilled syringe.

Extrusion: thick sheet, sheet, pipe, straw, strapping, Stationery sheet, BOPP Film, thin sheet, band.

Blow Molding: bottles.

Thermoforming: tray, bowl, jelly cup, water cups.

Flat yarn: woven bag, jumbo bag, carpet.

Fiber: multifilament, carpet, Spundbond, non-wovens.

Film: Cast film (CPP), Blown film (IPP).

An

 

Buyer Product Name Price Quantity Order Time(GMT+8)

Feedback most closely related to this product:

Email to this supplier
Verified Supplier | Ren County Qida Rubber Co., Ltd.
[ Hebei, China (Mainland) ]
Business Type: Manufacturer, Trading Company
  • Onsite operations checked and legal status confirmed

Communicate with Supplier

Ms. Annie Lee
What can I do for you?
Minisite Survey

Source on Alibaba.com

Over 2 Million Suppliers Easily Access Verified Suppliers Safe and Simple Trade Solutions Learn more